hollow glass molecular sieve can be simultaneously adsorbed hollow glass of water and organic residues, the hollow glass even at very low temperature keeps clear and transparent, and can fully reduce the hollow glass caused by great changes in seasonal and diurnal temperature strong internal and external pressure difference, completely solve the ordinary insulating glass desiccant to hollow glass expansion or contraction caused by distorted broken problem, ask extend the service life of the hollow glass.
our company's production and production of hollow glass molecular sieve can be selective adsorption of air water molecular exclusion of nitrogen and oxygen, mainly used in the double layer of glass in the air drying. Our production of hollow glass desiccant with high strength, small bulk density. It is not easy to be broken and damaged in the process of transportation and use; the adsorption capacity of water and gas sulfide is large, but the adsorption capacity of N2 and O2 is very small. The surface of the product is hard and smooth, the dust is low and the flow performance is good.
a. product technical specifications
|
index item
|
unit
|
3A
|
4A
|
|
ball diameter
|
mm
|
1.0— 1.5
|
1.5— 2.0
|
1.0— 1.5
|
1.5— 2.0
|
|
aperture
|
nm
|
0.3
|
0.4
|
|
wear rate
|
%
|
≤ 0.2
|
≤ 0.2
|
|
bulk density
|
g/ml
|
≥ 0.68
|
≥ 0.68
|
|
static water adsorption
|
%
|
≥ 20
|
≥ 20
|
|
screening
|
(%)
|
≥ 97
|
≥ 97
|
|
dust
|
(PPM)
|
≤ 60
|
≤ 60
|
|
adsorption capacity of organic compounds
|
|
without
|
has
|
|
adsorption temperature rise
|
25g/25cc
|
≥ 35
|
≥ 35
|
|
compressive strength
|
N/
|
≥ 15
|
≥ 25
|
≥ 15
|
≥ 25
|
B. hollow glass special molecular sieve
dsorption of water in the insulating glass air layer when it is produced.
l hollow glass in the life period of continuous adsorption into the layer of water in the air, to keep low dew point in insulating glass (C 60). Window installation, water into the air layer for 4 reasons.
1, improper disposal of aluminum frame angle;
2, sealant construction before dragging;
3, temperature changes lead to the increase of the deflection of insulating glass;
4, moisture permeability of sealant.
l the use of inert gases (argon and nitrogen) can improve energy efficiency. In order to reduce the noise and improve the effect of heat transfer, the use of six fluoride sulfur instead of air, the hollow glass molecular sieve on the almost no adsorption of sulfur dioxide six.
C. can be customized for special specifications
D. 25 25kg; packaging: carton or drum packaging, according to specific user requirements.
note: avoid direct exposure of molecular sieve air.
hollow glass molecular sieve can be simultaneously adsorbed hollow glass of water and organic residues, the hollow glass even at very low temperature keeps clear and transparent, and can fully reduce the hollow glass caused by great changes in seasonal and diurnal temperature strong internal and external pressure difference, completely solve the ordinary insulating glass desiccant to hollow glass expansion or contraction caused by distorted broken problem, ask extend the service life of the hollow glass.
our company's production and production of hollow glass molecular sieve can be selective adsorption of air water molecular exclusion of nitrogen and oxygen, mainly used in the double layer of glass in the air drying. Our production of hollow glass desiccant with high strength, small bulk density. It is not easy to be broken and damaged in the process of transportation and use; the adsorption capacity of water and gas sulfide is large, but the adsorption capacity of N2 and O2 is very small. The surface of the product is hard and smooth, the dust is low and the flow performance is good.
a. product technical specifications
|
index item
|
unit
|
3A
|
4A
|
|
ball diameter
|
mm
|
1.0— 1.5
|
1.5— 2.0
|
1.0— 1.5
|
1.5— 2.0
|
|
aperture
|
nm
|
0.3
|
0.4
|
|
wear rate
|
%
|
≤ 0.2
|
≤ 0.2
|
|
bulk density
|
g/ml
|
≥ 0.68
|
≥ 0.68
|
|
static water adsorption
|
%
|
≥ 20
|
≥ 20
|
|
screening
|
(%)
|
≥ 97
|
≥ 97
|
|
dust
|
(PPM)
|
≤ 60
|
≤ 60
|
|
adsorption capacity of organic compounds
|
|
without
|
has
|
|
adsorption temperature rise
|
25g/25cc
|
≥ 35
|
≥ 35
|
|
compressive strength
|
N/
|
≥ 15
|
≥ 25
|
≥ 15
|
≥ 25
|
B. hollow glass special molecular sieve
dsorption of water in the insulating glass air layer when it is produced.
l hollow glass in the life period of continuous adsorption into the layer of water in the air, to keep low dew point in insulating glass (C 60). Window installation, water into the air layer for 4 reasons.
1, improper disposal of aluminum frame angle;
2, sealant construction before dragging;
3, temperature changes lead to the increase of the deflection of insulating glass;
4, moisture permeability of sealant.
l the use of inert gases (argon and nitrogen) can improve energy efficiency. In order to reduce the noise and improve the effect of heat transfer, the use of six fluoride sulfur instead of air, the hollow glass molecular sieve on the almost no adsorption of sulfur dioxide six.
C. can be customized for special specifications
D. 25 25kg; packaging: carton or drum packaging, according to specific user requirements.
note: avoid direct exposure of molecular sieve air.